QuakeWrap, Inc. 
6840 South Tucson Boulevard
Tucson, AZ 85756 
United States 
800-782-5397 
520-791-7000
Visit this company's website


Facility : San Diego, CA

Protective (Barrier) Materials

    Water Water
  Water Contact Contact Contact
Trade Designation Size Restriction Temp Material

Coatings - Tank
QuakeWrap™[1] >= 5,000 gal. CLD 23 FRP

[1] Coating details:
    First Layer: Silica / QuakeBond™ J300SR (Tack Coat)
    Mix ratio (Silica:Resin): 1:1 by volume
    Maximum Field Use Dry Film Thickness (in mils): 40
    Final Cure Time and Temperature (before second layer): None
    
    Second Layer: QuakeBond™ J300SR (Saturating Resin)
    Mix ratio (A:B): 2:1 by volume (or 100:43 by weight)
    Saturation rate of QuakeWrap™ VU18C carbon fabric is maximum 50% by volume of saturating
    resin, i.e. [vol. of resin/vol. of resin and fabric] <= 0.5 
    Maximum Field Use Dry Film Thickness (mils): 50
    Maximum Number of Layers: 4 (1 layer contains tack coat, saturating resin, and carbon
    fabric)
    Final Cure Time and Temperature (after final layer of saturated fabric is applied): 72
    hours at ambient temperature
    
    Product shall be flushed for 1 hour at 10 gallons per minute prior to use.
    
    Maximum Total Dry Film Thickness (mils): 90

Coatings - Pipe - Immediate Return to Service
QuakeWrap™[1] >= 8" CLD 23 FRP

[1] Coating details:
    First Layer: Silica / QuakeBond™ J300SR (Tack Coat)
    Mix ratio (Silica:Resin): 1:1 by volume
    Maximum Field Use Dry Film Thickness (in mils): 40
    Final Cure Time and Temperature (before second layer): None
    
    Second Layer: QuakeBond™ J300SR (Saturating Resin)
    Mix ratio (A:B): 2:1 by volume (or 100:43 by weight)
    Saturation rate of QuakeWrap™ VU18C carbon fabric is maximum 50% by volume of saturating
    resin, i.e. [vol. of resin/vol. of resin and fabric] <= 0.5 
    Maximum Field Use Dry Film Thickness (mils): 50
    Maximum Number of Layers: 4 (1 layer contains tack coat, saturating resin, and carbon
    fabric)
    Final Cure Time and Temperature (after final layer of saturated fabric is applied): 72
    hours at ambient temperature
    
    Product shall be flushed for 1 hour at 10 gallons per minute prior to use.
    
    Maximum Total Dry Film Thickness (mils): 90

Coatings - Pipe
StifPipe™ >= 8" CLD 23 FRP
QuakeWrap™[1] >= 8" CLD 23 FRP

[1] Coating details:
    First Layer: Silica / QuakeBond™ J300SR (Tack Coat)
    Mix ratio (Silica:Resin): 1:1 by volume
    Maximum Field Use Dry Film Thickness (in mils): 40
    Final Cure Time and Temperature (before second layer): None
    
    Second Layer: QuakeBond™ J300SR (Saturating Resin)
    Mix ratio (A:B): 2:1 by volume (or 100:43 by weight)
    Saturation rate of QuakeWrap™ VU18C carbon fabric is maximum 50% by volume of saturating
    resin, i.e. [vol. of resin/vol. of resin and fabric] <= 0.5 
    Maximum Field Use Dry Film Thickness (mils): 50
    Maximum Number of Layers: 4 (1 layer contains tack coat, saturating resin, and carbon
    fabric)
    Final Cure Time and Temperature (after final layer of saturated fabric is applied): 72
    hours at ambient temperature
    
    Product shall be flushed for 1 hour at 10 gallons per minute prior to use.
    
    Maximum Total Dry Film Thickness (mils): 90