NSF Product and Service Listings

[1] Certified for a maximum exposed surface area of 25 sq. in./1000 gal.
[2] Certified for a maximum exposed surface area of 216 sq. in./1000 gal.

[2] Certified for a maximum exposed surface area of 216 sq. in./1000 gal.
[3] Certified for a maximum surface area of 568 square inches per 1000 gallons.  Mix ratio
    2:1 (Resin:Cure).

[1] Product is applied in multiple layers with Layers 1,2, and 3 optional:
    Protective (Barrier) Materials
    Layer 1: CSS-ES Epoxy Primer and Saturant apply 10 wet mils maximum.  Mix ratio of Part
    A to B is 2:1 by volume.  Mix with a drill and mixing paddle until uniformly blended (5
    minutes at 500 rpm).  Apply 1 coat.
    Layer 2: CSS-EP Paste Filler apply 40 wet mils maximum.  Mix ratio of Part A to B is 2:1
    by volume.  Mix with a drill and mixing paddle until uniformly blended (5 minutes at 500
    rpm). Apply 1 coat.
    Layer 3: CSS-CUGF27 Fabric saturated with CSS-ES Epoxy Primer and Saturant (follow
    mixing instructions above).  Apply with maximum thickness of 50 mils.  It is permitted
    to place Layer 3 between layers of carbon fabric (Layers 4+).
    Layer 4+: CSS-CUCF11, CSS-CUCF22, or CSS-CUCF44 Fabric saturated with CSS-ES Epoxy
    Primer and Saturant (follow mixing instructions above).  Apply 1 - 10 layers with a
    maximum thickness of 20 mils per layer of CSS-CUCF11, 40 mils per layer of CSS-CUCF22,
    or 80 mils per layer of CSS-CUCF44.
    Saturation rate for fabrics:  1 gallon per 75 square feet of CSS-CUCF11; 1 gallon per 50
    square feet of CSS-CUCF22; 1 gallon per 50 square feet of CSS-CUGF27; and 1 gallon per
    25 square feet of CSS-CUCF44.
    Final cure time is 72 hours at 70°F after application of final layer.  There is no cure
    between the application of layers.

[2] Product is applied in 5 layers:
    Combine the contents of V-Wrap 770-A pail and V-Wrap 770-B pail together and mix for 3
    minutes using a mixer speed of 400-600 RPM until
    uniformly blended. Transfer the mixed epoxy into the other pail and mix for an
    additional 2 minutes.
    Layer 1: 10 wet mils of V-Wrap 770 resin. Mix ratio of V-Wrap 770 resin part A:B is
    100:33 by weight.
    Layer 2: 40 wet mils of thickened V-Wrap 770 resin. Thickened V-Wrap 770 is achieved by
    adding fumed silica to the resin at a maximum ratio of 1.5
    parts fumed silica to 1 part resin by volume.
    Layer 3: 8 coats of V-Wrap EG50 or V-Wrap EG50B Fabric saturated with V-Wrap 770 resin.
    The thickness of each coat/layer of fabric is 50 mils.
    Layer 4: 8 coats of V-Wrap C100H, V-Wrap C200H, or V-Wrap C400H Fabric saturated with
    V-Wrap 770 resin. The thickness of each coat/layer of fabric is 90 mils.
    Layer 5: 40 wet mils of thickened V-Wrap 770 resin. Thickened V-Wrap 770 is achieved by
    adding fumed silica to the resin at a maximum ratio of 1.5
    parts fumed silica to 1 part resin by volume.
    The final cure time and temperature is 24 hours at 75ºF. There is no cure time required
    between the application of layers.

[1] Product is applied in multiple layers with Layers 1,2, and 3 optional:
    Protective (Barrier) Materials
    Layer 1: CSS-ES Epoxy Primer and Saturant apply 10 wet mils maximum.  Mix ratio of Part
    A to B is 2:1 by volume.  Mix with a drill and mixing paddle until uniformly blended (5
    minutes at 500 rpm).  Apply 1 coat.
    Layer 2: CSS-EP Paste Filler apply 40 wet mils maximum.  Mix ratio of Part A to B is 2:1
    by volume.  Mix with a drill and mixing paddle until uniformly blended (5 minutes at 500
    rpm). Apply 1 coat.
    Layer 3: CSS-CUGF27 Fabric saturated with CSS-ES Epoxy Primer and Saturant (follow
    mixing instructions above).  Apply with maximum thickness of 50 mils.  It is permitted
    to place Layer 3 between layers of carbon fabric (Layers 4+).
    Layer 4+: CSS-CUCF11, CSS-CUCF22, or CSS-CUCF44 Fabric saturated with CSS-ES Epoxy
    Primer and Saturant (follow mixing instructions above).  Apply 1 - 10 layers with a
    maximum thickness of 20 mils per layer of CSS-CUCF11, 40 mils per layer of CSS-CUCF22,
    or 80 mils per layer of CSS-CUCF44.
    Saturation rate for fabrics:  1 gallon per 75 square feet of CSS-CUCF11; 1 gallon per 50
    square feet of CSS-CUCF22; 1 gallon per 50 square feet of CSS-CUGF27; and 1 gallon per
    25 square feet of CSS-CUCF44.
    Final cure time is 72 hours at 70°F after application of final layer.  There is no cure
    between the application of layers.

[1] Product is applied in multiple layers with Layers 1,2, and 3 optional:
    Protective (Barrier) Materials
    Layer 1: CSS-ES Epoxy Primer and Saturant apply 10 wet mils maximum.  Mix ratio of Part
    A to B is 2:1 by volume.  Mix with a drill and mixing paddle until uniformly blended (5
    minutes at 500 rpm).  Apply 1 coat.
    Layer 2: CSS-EP Paste Filler apply 40 wet mils maximum.  Mix ratio of Part A to B is 2:1
    by volume.  Mix with a drill and mixing paddle until uniformly blended (5 minutes at 500
    rpm). Apply 1 coat.
    Layer 3: CSS-CUGF27 Fabric saturated with CSS-ES Epoxy Primer and Saturant (follow
    mixing instructions above).  Apply with maximum thickness of 50 mils.  It is permitted
    to place Layer 3 between layers of carbon fabric (Layers 4+).
    Layer 4+: CSS-CUCF11, CSS-CUCF22, or CSS-CUCF44 Fabric saturated with CSS-ES Epoxy
    Primer and Saturant (follow mixing instructions above).  Apply 1 - 10 layers with a
    maximum thickness of 20 mils per layer of CSS-CUCF11, 40 mils per layer of CSS-CUCF22,
    or 80 mils per layer of CSS-CUCF44.
    Saturation rate for fabrics:  1 gallon per 75 square feet of CSS-CUCF11; 1 gallon per 50
    square feet of CSS-CUCF22; 1 gallon per 50 square feet of CSS-CUGF27; and 1 gallon per
    25 square feet of CSS-CUCF44.
    Final cure time is 72 hours at 70°F after application of final layer.  There is no cure
    between the application of layers.